oxidized bitumen 95/25

Description of oxidized bitumen 95/25

Oxidized Bitumen 95/25 is Semi Solid grade of pure petroleum bitumen manufactured by air-blowing through an asphalt flux. Special physical properties of its grade can be used in different applications in the construction business. Oxidized bitumen 95/25 is based on petroleum bitumen which is made by oxidized bitumen 60/70 by very hot air. The numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value is the degrees Centigrade measured by the Ring and Ball method as determined by ASTM D36. The penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.

oxidized Bitumen is industrial bitumen which is dark, petroleum residue modified by the oxidation process. Oxidized Bitumen is produced by passing air through bitumen under controlled temperature conditions. Its consistency ranges from highly viscous to solid. Blown bitumen grade has technical advantages such as durability, flexibility, water resistant and chemical stability. There is the different grade of blown bitumen.
BITUMENSHOP Company guaranty the quality of BITUMENSHOP Oxidized bitumen
95/25 with the arrangement of the international inspector to check quality and quantity of the bitumen 95/25 during the loading to the vessel and controlling the production by QC by batch test report before shipping. BITUMENSHOP Company guarantees the quality to meet with ASTM.

Uses of oxidized bitumen 95/25

Oxidized bitumen 95/25 uses in the chemical, fuel, paints, lacquers, varnishes, paper-pulp-board, textile processing, road construction, pavement ,crack seal and repairmen, civil works, roofing, construction industries; sealing and insulating buildings, adhesive, construction materials additive, dust-binding, insulating and impregnating agent, make rubber and plastic products. The oxidized bitumen 95/25 products are for paving. also used in asphalt-based paints for corrosion protection of metals, in lining public works structures, adhesives in electrical laminates, base for synthetic turf; typical uses for bitumen 95/25 used also for water-proof application and corrosion resistance for pipe coating, Portland cement pavement, hydraulic applications, paint manufacturing, caulking, mastics, and damp proofing. bitumen 95/25 is using insulation and isolation bitumen membrane sheet. Also, Car undercoating Automobile industry is specially required for Blown Asphalt. Vehicle undercoating material is based on Bitumen. Bitumen provides excellent waterproof, dust proof and noise proof for automobile undercoating.

Application of oxidized bitumen 95/25

Oxidized bitumen 95/25 should be heated double temperature against the softening point to be able to have flow and viscosity. To use bitumen 95/25, surfaces must be dry, clean and free of loose particles, formwork, curing products, irregularities, slurry, etc.

Storage/handling of oxidized bitumen 95/25

bitumen 95/25 has 10 years validity with multi-time heating and cooling, please refer to MSDS.

Packing of oxidized bitumen 95/25

Various pickings are available for customer’s purpose and conveniences. BITUMENSHOP Co is the manufacturer of oxidized bitumen 95/25 in various packing including Kraft bag, meltable plastic bag, drum, and bulk bitumen 95/25 from penetration grade bitumen, which is blown by hot air in a controlled process until the desired specification is reached. BITUMENSHOP oxidized bitumen 95/25 can be supplied in any grade and are designated by two numbers to indicate the softening point and penetration ranges. The bitumen grade 95/25 means the softening point is 95°c and penetration is 15 desi millimeter is produced in compliance and conformity with ASTM standard and meets the following specification.

Specification of oxidized bitumen 95/25

Analysis bitumen 95/25

Bitumen 95/25

Test method



Specific gravity @25/25 C



1.05 approx.

Penetration @ 25°c




Softening point °c




Loss on heating(wt) %


Wt. %

0.2 max

Flashpoint °c



250 min

Solubility is CS2(wt) %


Wt. %

99.5 max

Spot test